GB Cr12 JIS SKD1 DIN 1.2080 ASTM D3 Forged Cold Work Tool Steel
1: AISI D3 steel introduction
AISI D3 cold work steel, also know as DIN 1.2080 (Werkstoff) and
JIS SKD1, is a 12% chrome alloy steel. D3 cold work steelhas very
high wear resistance against abrasive and adhesive wear due to the
high volume of hard carbides in the steel matrix, medium toughness,
dimensionally stable, high compressive strength, not secondary
hardenable. Type AISI D3 cold works tool steel is oil-quenched;
though small sections can be gas quenched after austenitization
using vacuum. As a result, tools made with type D3 cold work tool
steel tend to be brittle during hardening.
2: AISI D3 Steel equivalent
| Country | China | Japan | Germany | USA | UK |
| Standard | GB/T 1299 | JIS G4404 | DIN EN ISO4957 | ASTM A681 | BS4659 |
3: AISI D3 steel chemical composition
| Grade | C | Mn | P | S | Si | Cr | V | T | Mo |
D3
| 2.00 | 2.35 | 0.10 | 0.60 | 0.03 | 0.03 | 0.10 | 0.60 | 11.00 | 13.50 | - | 1.10 | - | 1.00 | - | - |
| 1.2080/X210C | 1.90 | 2.20 | 0.20 | 0.60 | | | 0.10 | 0.60 | 11.00 | 13.00 | - | - | - | - | - | - |
| SKD1 | 1.90 | 2.20 | 0.20 | 0.60 | 0.03 | 0.03 | 0.10 | 0.60 | 11.00 | 13.00 | - | - | - | - | - | - |
4: AISI D3 steel mechanical properties
The mechanical properties mainly include tensile strength, yield
strength, elongation, area or reduction, hardness, impact value,
non-metalic inclusion etc.
Different heat treatment, the mechanical properties will be
different, such as normalized, tempered, QT.
5: AISI D3 steel overviews
| Size | Round | Dia 6-1200mm |
| Plate/Flat/Block | Thickness 6mm-500mm |
Width 20mm-1000mm |
| Process | EAF+LF+VD+Forged+Heat treatment(optiomal) |
Heat treatment | Normalized;Annealed;Quenched;Tempered |
Suface condition | Black;Peeled;Polished;Machined;Grinded;Turned;Milled |
Delivery condition | Forged;Hot rolled;Clod drawn |
| Test | Tensile strength, Yield strength, elongation, area of reduction,
impact value, hardness,
grain size, ultrasonic test, US inspection, magnetic particle
testing, etc. |
Payment terms | T/T:L/C;/Money gram/ Paypal |
Trade terms | FOB: CIF: C&F; etc.. |
| Packing | Standard Packages, or as Customers Request |
Delivery time | 30-45 days |
| Application | D3 is suitable for applications such as complex blanking and
forming tools for long runs
and for hard and abrasive materials. |
6: Delivery condition
For hot forged or hot rolled bar, usually the delivery condition is
hot forged or rolled, annealed, rough turned.
For hot forged plate, usually the delivery condition is hot forged,
annealed, milled surface.
For hot rolled plate, usually the delivery condition is hot rolled,
annealed, black surface.
7.Heat treatment
Isothermal annealing:
- Heat to 800°Cand hold at temperature for 1/2 h to 1 h;
- Furnace cooling to 670°Cand hold at temperature for at least 10
hours;
- Cool by 10°C/h to 630°C;
- Cooling in air.
Maximum hardness:≤240 HB
Stress relieving:
To be carried out after maching before the final heat treatment.
- Heat to 600-650°C, hold for 4-6 hours;
- Cooling in furnace to 300-350°C;
- Cooling in air
Hardening:
- Initial preheating to 350-450°C;
- Second preheating to 650-750°C;
- Heat to hardening temperature 860-890°Cand hold at temperature;
- Cooling in hot oil (40-60°C); oil quenched hardness: 54-59HRC;
Tempering:
Tempering must be carried out within one hour from hardening(warm
part) in the range 550-630°Cfor 4-6 hours according to hardness
required, the dimensions of the parts and operating conditions.